Study Effect of annealing Temperature on enhancement of High-Tc Phase for BiPbSrCaCuZnO thin film through thermal expantion
DOI:
https://doi.org/10.23851/mjs.v29i4.190Keywords:
BiPbSrCaCuZnO super conducting thin film thermal expansionAbstract
Annealing thermal plays an important role on the formation of high Tc-phase BiPbSrCaCuZnO through expansion and contraction layers which be associated with formation high and low phases respectively, The prepared samples composition BiPbSrCaCuZnO have been annealed at (820,840,860,880) C°. It is observed the critical temperature Tc increase for films which annealed at (820,840,880) C°while Tc decreases at Ta =860 C°.Downloads
References
• [1] –K.Fossheim and A.Sudbo, superconductivity-physics and Applicatons,Joha willey and sons Ltd.(2005).
• [2] – H.Aydin, O.Cakirogln, M.Nurosy, and C.Terzioglul,47,2,(2009).
• [3]–A.A.Hussein “Cobalt substitution effect on (Bi,Pb)-2223 superconducting Compound” MSC,Thesis, Baghdad university college of science,(2016).
• [4]–H.A.Thabit “Mechanical Properties of superconductor (BiPbSrBaCa CuNiO)”Msc, Thesis, Baghdad university college of science,(2011).
• [5]–S.A.Halim, S.S.H.Ravandi,M.I.Adam,S.K.Chen and K.P.Lim, Sci.Technol.,18,1,P.266,(2010).
• [6]-S.M.Khalil,Effects of optimum annealing time on superconducting properties of BiPbSrCaCuO system,phys.stat.Sol.178,p.731,(2000).
• [7]-Nayera Hassan Mohammed, Ramadan Awad,Ali Ibrahim Abou Aly,etc physics Department ,Faculty,Alexandria,Egypt. Accepted February 9th,(2012).
• [8]-M.M.Ibrahim,N.M.Megahid, M.M.Abd EL-Raheem, S.M.Khail” Preparation and characterization of Hot-Pressed and sintered BiPbSrCaCuO superconductor”,Department of physics,Faculty of science, Sohag University, V.2,P.75,(2012).
Downloads
Key Dates
Published
Issue
Section
License
Articles accepted for publication in Al-Mustansiriyah Journal of Science (MJS) are protected under the Creative Commons Attribution 4.0 International License (CC BY-NC). Authors of accepted articles are requested to sign a copyright release form prior to their article being published. All authors must agree to the submission, sign copyright release forms, and agree to be included in any correspondence between MJS and the authors before submitting a work to MJS. For personal or educational use, permission is given without charge to print or create digital copies of all or portions of a MJS article. However, copies must not be produced or distributed for monetary gain. It is necessary to respect the copyright of any parts of this work that are not owned by MJS.