Study Effect of annealing Temperature on enhancement of High-Tc Phase for BiPbSrCaCuZnO thin film through thermal expantion

suzan malek, suzan malek shakouli

Abstract


Annealing thermal plays an important role on the formation of high Tc-phase BiPbSrCaCuZnO through expansion and contraction layers which be associated with formation high and low phases respectively, The prepared samples composition BiPbSrCaCuZnO have been annealed at (820,840,860,880) C°.
It is observed the critical temperature Tc increase for films which annealed at (820,840,880) C°while Tc decreases at Ta =860 C°.

Keywords


BiPbSrCaCuZnO super conducting thin film thermal expansion

Full Text:

PDF

References


• [1] –K.Fossheim and A.Sudbo, superconductivity-physics and Applicatons,Joha willey and sons Ltd.(2005).

• [2] – H.Aydin, O.Cakirogln, M.Nurosy, and C.Terzioglul,47,2,(2009).

• [3]–A.A.Hussein “Cobalt substitution effect on (Bi,Pb)-2223 superconducting Compound” MSC,Thesis, Baghdad university college of science,(2016).

• [4]–H.A.Thabit “Mechanical Properties of superconductor (BiPbSrBaCa CuNiO)”Msc, Thesis, Baghdad university college of science,(2011).

• [5]–S.A.Halim, S.S.H.Ravandi,M.I.Adam,S.K.Chen and K.P.Lim, Sci.Technol.,18,1,P.266,(2010).

• [6]-S.M.Khalil,Effects of optimum annealing time on superconducting properties of BiPbSrCaCuO system,phys.stat.Sol.178,p.731,(2000).

• [7]-Nayera Hassan Mohammed, Ramadan Awad,Ali Ibrahim Abou Aly,etc physics Department ,Faculty,Alexandria,Egypt. Accepted February 9th,(2012).

• [8]-M.M.Ibrahim,N.M.Megahid, M.M.Abd EL-Raheem, S.M.Khail” Preparation and characterization of Hot-Pressed and sintered BiPbSrCaCuO superconductor”,Department of physics,Faculty of science, Sohag University, V.2,P.75,(2012).




DOI: http://dx.doi.org/10.23851/mjs.v29i4.190

Refbacks

  • There are currently no refbacks.


Copyright (c) 2019 Al-Mustansiriyah Journal of Science

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

Copyright (c) 2018 by Al-Mustansiriyah Journal of Science
ISSN: 1814-635X (Print), ISSN: 2521-3520 (online)